Sanicro71 是一种具有正常金属回收率的碱性药皮焊条，用于焊接 NiCrFe 合金、9%Ni 钢以及用于低温环境的镍合金钢。它还用于异种接头，例如，不锈钢和 NiCu 合金与碳钢和镍合金之间的焊接。Sanicro71 具有以下特点：低飞溅 和良好的脱渣性。
STANDARDS
产品认证
– ISO: 14172:Ni6182
– AWS A5.11/ASME SFA-5.11:ENiCrFe-3
– W.Nr.: 2.4807
– TÜV
APPLICATIONS
Applications for Sanicro 71 are found inconstructions to be used at low temperature; e.g. Ni-steel with aCr content of 3.5 %, 5 % and 9 % are used as well as austeniticCr-Ni stainless steel, especially if the weld metal isto be thermoformed or stressrelieved.
Sanicro 71 is suitable for joining nickelalloys such as:
The alloy can be used in air up to 1200°C(2150°F), in sulphur dioxide atmospheres up to 800°C (1470°F) andin ammonia at the highest process temperature.This alloy is used for surfacing or joining where there arestrict requirements on stress corrosion resistanceand for high temperature service.
®
®
– Sandvik Sanicro 30 (UNS N08800, EN 1.4558,mod Alloy 800) ®
– Sandvik Sanicro 31H (UNS N08810, EN1.4958, Alloy 800H) ®
– Sandvik Sanicro 70 (UNS N06600, EN 2.4816,Alloy 600) ®
焊缝金属特征
以下数据对非热处理的全焊缝金属有效。
C Si Mn P S Cr Ni Mo Nb FeCu
化学成分，wt%
≤0.05 ≤1.0 6.5 ≤0.015 ≤0.010 16 67 ≤1.5 2.5≤10 ≤0.5
微观组织全焊缝金属
全奥氏体。
机械性能
温度 C (°F) 20 (68) -196(-320)
屈服强度，R MPa (ksi) >360(52) -
抗拉强度，R MPa (ksi) >620(90) -
延伸率，A %>30 -
冲击强度，夏比 V 型 J(ft lb) >60 (44) >45
R 对应于 0.2% 塑型变形的屈服强度
o
P0.2a
m
a p0.2
耐腐蚀性能
根据 ASTM A262 practiceE，在“焊态”、应力消除和固溶退火状态下的抗晶间腐蚀性。
制造
直径，mm(in.) 电流，A
2.50 (~3/32) 45-60
3.25 (~1/8) 70–95
4.00 (~5/32) 90-120
5.00 (~3/16)120-150
必要时重新烘干焊条：200°C (390°F)/2 h
生产率数据
焊条直径，mm (in.) 2.50 (~3/32) 3.25 (~1/8) 4.00(~5/32) 5.00 (~3/16)
长度，mm (in.) 300 (~12) 350 (~14) 350 (~14) 350(~14)
重量
kg (lb)/100 pcs 1.7 (3.7) 2.9 (6.4) 5.0 (11)8.7 (19.1)
kg (lb)/箱 4.5 (9.9) 4.6 (10.1) 5.3 (11.7) 5.2(2.4)
焊条数/箱 260 160 105 58
有效值
kg 焊缝金属/kg 焊条 0.61 0.71 0.68 0.67
lb 焊缝金属/lb 焊条 0.61 0.71 0.68 0.67
变化值
焊条/kg 焊缝金属 94 49 29 16
焊条/lb 焊缝金属 43 23 13 7
每根焊条在Zui大电流下的熔化时间 (s) 46 59 76101
工作数据
焊接位置， 除立向下焊之外的所有焊接位置
电流/极性 直流电/焊条正极。